LCD Display Portable Leeb Hardness Tester With Rechargeable Li-battery
TECHNICAL DATA
Measuring Materials | Steel and cast steel, alloy tool steel, stainless steel, gray cast iron, nodular cast iron, cast aluminum alloy, copper zinc alloys (brass), copper and tin alloy, copper (bronze), forged steel |
Measuring Range | HLD(170~960), HRC(17.9~69.5), HB(19~683), HV(80~1042), HS(30.6~102.6), HRA(59.1~88), HRB(13.5~101.7) |
Indication Error | ±6HLD (D impact device) |
Measuring Direction | 360° |
Hardness Scale | HL, HB, HRB, HRC, HRA, HV, HS |
Display | 128*64 digital matrix LCD |
Data Memory | Max 600 groups (relative to impact times 1~32 adjustable) |
Power | Rechargeable li-battery |
Working Temperature | -20°C~55°C |
Size | 210x85x45mm |
Weight | 0.6kg |
MAIN FEATURE
*Built-in printer, can print testing results any time;
*Test at any angle, even upside down;
*Has a starting value calibration function, ensure the data is applicable and accurate in different codes and standards;
*Seven impact devices are available for special application. Automatically identify the type of impact devices;
*User calibration function;
*Battery information indicates the rest capacity of the battery and the charge status;
*Has the function of automatic alarm. Pre-set tolerance limit, beyond the range has automatic alarm, especially suitable for batch testing;
*Menu operation, information rich, intuitive, the realization of arbitrary switching material and hardness of system's key type, simple and convenient;
*Excellent after-sale service system for high quality products-two years warranty and all life maintenance. Easy to operate;
*Narrow space also available to use;
*Support OEM Service;
*High price performance.
STANDARD DELIVERY
ITEM | QTY |
KH520 Host | 1 PC |
Standard D Impact Device | 1 PC |
Standard Calibration Block | 1 PC |
Standard Support Ring | 1 PC |
Brush | 1 PC |
USB Cable | 1 PC |
PC Software | 1 PC |
User Manual | 1 PC |
Instrument Case | 1 PC |
Warranty | 2 Years |
Type of Impact Device | DC(D)/DL | D+15 | C | G | E |
Impacting energy Mass of impact body | 11mJ 5.5g/7.2g | 11mJ 7.8g | 2.7mJ 3.0g | 90mJ 20.0g | 11mJ 5.5g |
Test tip hardness: Dia. Test tip: Material of test tip: | 1600HV 3mm Tungsten carbide | 1600HV 3mm Tungsten carbide | 1600HV 3mm Tungsten carbide | 1600HV 5mm Tungsten carbide | 5000HV 3mm synthetic diamond |
Impact device diameter: Impact device length: Impact device weight: | 20mm 86(147)/75mm 50g | 20mm 162mm 80g | 20mm 141mm 75g | 30mm 254mm 250g | 20mm 155mm 80g |
Max. hardness of sample | 940HV | 940HV | 1000HV | 650HB | 1200HV |
Mean roughness value of sample surface Ra: | 1.6μm | 1.6μm | 0.4μm | 6.3μm | 1.6μm |
Min. weight of sample: Measure directly with stand Need coupling tightly | >5kg 2~5kg 0.05~2kg | >5kg 2~5kg 0.05~2kg | >1.5kg 0.5~1.5kg 0.02~0.5kg | >15kg 5~15kg 0.5~5kg | >5kg 2~5kg 0.05~2kg |
Min. thickness of sample Coupling tightly: Min. layer thickness for surface hardening: |
5mm
≥0.8mm |
5mm
≥0.8mm |
1mm
≥0.2mm |
10mm
≥1.2mm |
5mm
≥0.8mm |
Size of tip indentation | ||||||
Hardness 300HV | Indentation diameter: Depth of indentation: |
0.54mm
24μm |
0.54mm
24μm |
0.38mm
12μm |
1.03mm
53μm |
0.54mm
24μm |
Hardness 600HV | Indentation diameter: Depth of indentation |
0.54mm
17μm |
0.54mm
17μm |
0.32mm
8μm |
0.90mm
41μm |
0.54mm
17μm |
Hardness 800HV | Indentation diameter: Depth of indentation |
0.35mm
10μm |
0.35mm
10μm |
0.35mm
7μm |
--
-- |
0.35mm
10μm |
Application | DC type used to measuring hole or inside face of cylinder, DL type used to measuring elongated narrow slot or hole, D type for routine measurements. | Suitable for measuring surface of the trench or concave. | Suitable for measuring thin workpiece and harden surface. | Suitable for heavy or rough castings and forgings. | Suitable high hardness material. |